• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please review our product specifications or consult the approval sheet for product specifications before ordering.
!Note
C85E.pdf
Jul.13,2011
DEB Series (SCpleacsisf2ic/aDtioCn1skVa-n3d.1T5eksVt)MSeptehcoifdicsations and Test Methods
Continued from the preceding page.
No.
Item
Appearance
Specifications
No marked defect
Test Method
First the capacitor should be
Capacitor
1.5
Thermal
Screen
stored at 120+0/-5°C for
60+0/-5 sec.
Char. B: Within ±5%
Char. E: Within ±15%
Char. F: Within ±20%
Capacitance
Change
Then, as in the figure, the lead
wires should be immersed in
solder of 260+0/-5°C up to 1.5 to
2.0mm from the root of terminal
for 7.5+0/-1 sec.
to 2.0mm
Molten
Solder
Soldering Effect
(On-Preheat)
13
Dielectric Strength
(Between Lead
Wires)
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
then placed at room condition* for 24±2 hrs.
before initial measurements.
Per item 4.
Post-treatment: Capacitor should be stored for 4 to 24 hrs. at
room condition.*
Appearance
No marked defect
The capacitor should be subjected to 5 temperature cycles,
then consecutively to 2 immersion cycles.
<Temperature Cycle>
Char. B: Within ±10%
Char. E: Within ±20%
Char. F: Within ±30%
Capacitance
Change
Step Temperature (°C) Time (min)
1
2
3
4
-25±3
Room Temp.
85±3
30
3
30
3
Char. B, E: 4.0% max.
Char. F: 7.5% max.
D.F.
I.R.
Room Temp.
2000MΩ min.
Temperature
Cycle time: 5 cycles
14 and Immersion
Cycle
<Immersion Cycle>
Step Temperature (°C) Time (min) Immersion Water
1
2
65+5/-0
0±3
15
15
Clean water
Salt water
Dielectric Strength
(Between Lead
Wires)
Cycle time : 2 cycles
Per item 4.
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
then placed at room condition* for 24±2 hrs.
before initial measurements.
Post-treatment: Capacitor should be stored for 4 to 24 hrs. at
room condition.*
Appearance
No marked defect
Set the capacitor for 500+24/-0 hrs. at 40±2°C in 90 to 95%
relative humidity.
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
then placed at room condition* for 24±2 hrs.
before initial measurements.
Char. B: Within ±10%
Char. E: Within ±20%
Char. F: Within ±30%
Capacitance
Change
Humidity (Under
15
9
Steady State)
Char. B, E: 5.0% max.
Char. F: 7.5% max.
D.F.
Post-treatment: Capacitor should be stored for 1 to 2 hrs. at
room condition.*
I.R.
1000MΩ min.
Appearance
No marked defect
Apply the rated voltage for 500+24/-0 hrs. at 40±2°C in 90 to
95% relative humidity. (Charge/Discharge currentV50mA)
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
then placed at room condition* for 24±2 hrs.
Char. B: Within ±10%
Char. E: Within ±20%
Char. F: Within ±30%
Capacitance
Change
Humidity
16
Loading
before initial measurements.
Post-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
then placed at room condition* for 24±2 hrs.
Char. B, E: 5.0% max.
Char. F: 7.5% max.
D.F.
I.R.
500MΩ min.
Appearance
No marked defect
Apply a DC voltage of 150% of the rated voltage for
1000+48/-0 hrs. at 85±2°C with a relative humidity of 50% max.
(Charge/Discharge currentV50mA)
Pre-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
then placed at room condition* for 24±2 hrs.
before initial measurements.
Post-treatment: Capacitor should be stored at 85±2°C for 1 hr.,
then placed at room condition* for 24±2 hrs.
Char. B: Within ±10%
Char. E: Within ±20%
Char. F: Within ±30%
Capacitance
Change
17 Life
Char. B, E: 4.0% max.
Char. F: 7.5% max.
D.F.
I.R.
2000MΩ min.
* "Room condition" Temperature: 15 to 35°C, Relative humidity: 45 to 75%, Atmospheric pressure: 86 to 106kPa
48
MURATA [ muRata ]