（C－C2）
C2
×100（%）
C
：Capacitance in Step 1 or Step 3
C2 ：Capacitance in Step 2
9. Deflection
Appearance
: No abnormality
Standard
Capacitance change : Within ±5% or ±0.5 pF, whichever is larger.
Temperature
Compensating（Class1）
Appearance
: No abnormality
: Within±0.5 pF
High Frequency Type
Specified
Value
Cpaitance change
Appearance
: No abnormality
Capacitance change : Within ±12.5%（BJ, B7, C6, C7,LD(※)）
Within ±30%（F）
High Permittivity （Class2）
Note: ※LD Low distortion high value multilayer ceramic capacitor
Multilayer Ceramic Capacitors
042, 063, ※105 Type
The other types
Board
Glass epoxy-resin substrate
Test
Thickness
Warp
0.8mm
1.6mm
Methods and
Remarks
1mm
Duration
10 sec.
※105 Type thickness, C： 0.2mm ,P： 0.3mm.
Capacitance measurement shall be conducted
with the board bent
10. Body Strength
Standard
－
Temperature
Specified
Value
Compensating（Class1）
High Frequency Type No mechanical damage.
－
High Permittivity （Class2）
High Frequency Type
Applied force
Duration
: 5N
Test
: 10 sec.
Methods and
Remarks
11. Adhesive Strength of Terminal Electrodes
Temperature
Standard
Specified
Compensating（Class1）
High Frequency Type No terminal separation or its indication.
Value
High Permittivity （Class2）
Multilayer Ceramic Capacitors
042, 063 Type
2N
105 Type or more
5N
Test
Methods and
Remarks
Applied force
Duration
30±5 sec.
12. Solderability
Standard
High Frequency Type At least 95% of terminal electrode is covered by new solder.
Temperature
Specified
Value
Compensating（Class1）
High Permittivity （Class2）
Eutectic solder
H60A or H63A
230±5℃
Lead-free solder
Sn-3.0Ag-0.5Cu
245±3℃
Test
Solder type
Methods and
Remarks
Solder temperature
Duration
4±1 sec.
▶ This catalog contains the typical specification only due to the limitation of space. When you consider the purchase of our products, please check our specification.