Product Specification
No.
7.9
108-78140
PERFORMANCE
Wet Solder Coverage：
(Plated area only)
95% Min.
ITEM
Contact
Solderability
MEASUREMENT METHOD
Solder bath：Sn-40Pb
Matte Tin plating only
Solder Temperature：235±5℃
Solder bath：Sn-3Ag-0.5Cu
Immersion Duration：5±0.5sec.
Solder Temperature：250±5℃
Flux：Alpha100
Immersion Duration：5±0.5sec.
AMP Spec. 109-5203
Flux：ULF-300R
Contact crimped on free-length of wire is inserted into the proper location of
the plug housing. Holding position of the wire is 20mm apart from the crimp barrel.
Insertion speed is 100mm/min. or less.
7.10
7.11
7.12
7.13
7.14
Contact
Insertion
Characteristic
(Between
Contact and
Housing)
Contact
Withdrawal
Characteristic
(Between
Contact and
Housing)
Contact
Retention Force
(Between
Contact and
Housing)
Strength of
Crimp
Connection
(Between
Contact and
Wire)
Housing
Retention Force
(Housing
Locking
Strength)
Contact can be inserted without bending of
wire.
Withdraw the contact inserted under the condition of 6.10.
There shall be no detrimental binding,
crack and deformation.
About 100mm long wire is crimped with the plug housing connector and the receptacle 58.8N(6kgf) or more
contact is fastened and then the load that causes separation of contact from the
housing with the wire pulled toward the axis at a constant speed of
approx.100mm/min. is measured.
After the receptacle contact with wire crimped is fastened and then the load that Wire size
causes wire breakage or separation of the wire from the crimped barrel with the
0.5
wire pulled toward the axis at a constant speed of approx. 100mm/min. is measured.
0.85
1.25
88.2N (9kgf) or more
127.4N(13kgf) or more
176.4N(18kgf) or more
After the cap housing is fastened, mated plug housing is pulled at a constant The lock mechanism shall not get released
speed of approx. 100mm/min.
or broken less than 98N(10kgf).
Rev. A8
9 of 41
MACOM [ Tyco Electronics ]