Product specification
12
14
General Purpose & High Cap.
Y5V
6.3 V to 50 V
Surface-Mount Ceramic Multilayer Capacitors
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
IEC 60384- 4.11
21/22
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for
24 ±1 hours at room temperature
No visual damage
Rapid change
of
temperature
<General purpose series>
∆C/C
5 cycles with following detail:
Class2:
30 minutes at lower category temperature
30 minutes at upper category temperature
Y5V: ±20%
<High Capacitance series>
∆C/C
Recovery time 24 ±2 hours
Class2:
Y5V: ±20%
D.F. meet initial specified value
ins meet initial specified value
R
4.13
No visual damage after recovery
Damp heat
with Ur load
1. Preconditioning, class 2 only:
150 +0/-10 °C /1 hour, then keep for
24 ±1 hour at room temp
<General purpose series>
∆C/C
2. Initial measure:
Class2:
Spec: refer initial spec C, D, IR
Y5V: ±30%
3. Damp heat test:
500 ±12 hours at 40 ±2 °C;
90 to 95% R.H. 1.0 Ur applied
D.F.
Class2:
Y5V: ≤ 15%
4. Recovery:
Class 2: 24 ±2 hours
Rins
5. Final measure: C, D, IR
Class2:
Y5V: ≥ 500 MΩ or Rins x Cr ≥ 25s
whichever is less
P.S. If the capacitance value is less than the
minimum value permitted, then after the other
measurements have been made the capacitor shall
be precondition according to “IEC 60384 4.1” and
then the requirement shall be met.
<High Capacitance series>
∆C/C
Class2:
Y5V: ±30%
D.F.
Class2:
Y5V: 2 x initial value max
Rins
Class2:
Y5V: 500 MΩ or Rins x Cr ≥ 25s
whichever is less