Product specification
11
14
General Purpose & High Cap.
Y5V
6.3 V to 50 V
Surface-Mount Ceramic Multilayer Capacitors
TEST
TEST METHOD PROCEDURE
REQUIREMENTS
IEC 60384- 4.8
21/22
Mounting in accordance with IEC 60384-22
paragraph 4.3
No visible damage
Bond
strength of
plating on
end face
<General purpose series>
∆C/C
Conditions: bending 1 mm at a rate of 1 mm/s,
radius jig 340 mm
Class2:
Y5V: ±10%
<High Capacitance series>
∆C/C
Class2:
Y5V: ±10%
4.9
Precondition: 150 +0/–10 °C for 1 hour, then keep Dissolution of the end face plating shall not
Resistance to
soldering
heat
for 24 ±1 hours at room temperature
exceed 25% of the length of the edge
concerned
Preheating: for size ≤ 1206: 120 °C to 150 °C for 1
minute
<General purpose series>
Preheating: for size >1206: 100 °C to 120 °C for 1
minute and 170 °C to 200 °C for 1 minute
∆C/C
Class2:
Y5V: ±20%
Solder bath temperature: 260 ±5 °C
Dipping time: 10 ±0.5 seconds
Recovery time: 24 ±2 hours
<High Capacitance series>
∆C/C
Class2:
Y5V: ±20%
D.F. within initial specified value
Rins within initial specified value
4.10
Preheated the temperature of 80 °C to 140 °C and The solder should cover over 95% of the
Solderability
maintained for 30 seconds to 60 seconds.
critical area of each termination
Test conditions for lead containing solder alloy
Temperature: 235 ±5 °C
Dipping time: 2 ±0.2 seconds
Depth of immersion: 10 mm
Alloy Composition: 60/40 Sn/Pb
Number of immersions: 1
Test conditions for leadfree containing solder alloy
Temperature: 245 ±5 °C
Dipping time: 3 ±0.3 seconds
Depth of immersion: 10 mm
Alloy Composition: SAC305
Number of immersions: 1