Product specification
16
18
General Purpose & High Cap.
X5R
4 V to 50 V
Surface Mount Multilayer Ceramic Capacitors
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
IEC 60384- 4.11
21/22
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for 24 ±1 hours at
room temperature
No visual damage
Rapid Change
of
Temperature
<General purpose series>
∆C/C
5 cycles with following detail:
Class2:
30 minutes at lower category temperature
30 minutes at upper category temperature
X5R: ±15%
<High Capacitance series>
∆C/C
Recovery time 24 ±2 hours
Class2:
X5R: ±15%
D.F. meet initial specified value
R
ins meet initial specified value
4.13
No visual damage after recovery
Damp Heat
with Ur Load
1. Preconditioning, class 2 only:
150 +0/-10 °C /1 hour, then keep for 24 ±1 hour at
room temp
<General purpose series>
∆C/C
2. Initial measure:
Class2:
Spec: refer to initial spec C, D, IR
X5R: ±15%
3. Damp heat test:
500 ±12 hours at 40 ±2 °C;
90 to 95% R.H. 1.0 Ur applied
D.F.
Class2:
4. Recovery:
Class 2: 24 ±2 hours
X5R: ≤ 16V: ≤ 7%
≥ 25V: ≤ 5%
5. Final measure: C, D, IR
Rins
Class2:
P.S. If the capacitance value is less than the minimum
value permitted, then after the other measurements have
been made the capacitor shall be preconditioned
according to “IEC 60384 4.1” and then the requirements
shall be met.
X5R: ≥ 500 MΩ or Rins x Cr ≥ 25s
whichever is less
<High Capacitance series>
∆C/C
Class2:
X5R: ±20%
D.F.
Class2:
X5R: 2 x initial value max
Rins
Class2:
X5R: 500 MΩ or Rins x Cr ≥ 25s
whichever is less
www.yageo.com
Feb 10, 2012 V.12