Product specification
12
15
High-Voltage
NP0/X7R 1 KV to 3 KV
Surface-Mount Ceramic Multilayer Capacitors
TEST
TEST METHOD PROCEDURE
REQUIREMENTS
IEC 60384- 4.7
21/22
A force applied for 10 seconds to the line joining
the terminations and in a plane parallel to the
substrate
Force
size ≥ 0603: 5N
Adhesion
4.8
Mounting in accordance with IEC 60384-22
paragraph 4.3
No visible damage
Bond
Strength of
Plating on
End Face
Conditions: bending 1 mm at a rate of 1 mm/s,
radius jig 340 mm
∆C/C
Class 1:
NP0: within ±1% or 0.5 pF, whichever is greater
Class2:
X7R: ±10%
4.9
Precondition: 150 +0/–10 °C for 1 hour, then
keep for 24 ±1 hours at room temperature
Dissolution of the end face plating shall not
exceed 25% of the length of the edge
concerned
Resistance to
Soldering
Heat
Preheating: for size ≤ 1206: 120 °C to 150 °C for
1 minute
∆C/C
Preheating: for size >1206: 100 °C to 120 °C for
1 minute and 170 °C to 200 °C for 1 minute
Class 1:
NP0: within ±0.5% or 0.5 pF, whichever is greater
Solder bath temperature: 260 ±5 °C
Dipping time: 10 ±0.5 seconds
Recovery time: 24 ±2 hours
Class2:
X7R: ±10%
D.F. within initial specified value
Rins within initial specified value
4.10
Preheated to a temperature of 80 °C to 140 °C
and maintained for 30 seconds to 60 seconds.
The solder should cover over 95% of the critical
area of each termination
Solderability
1. Temperature: 235±5°C / Dipping time: 2 ±0.5 s
2. Temperature: 245±5°C / Dipping time: 3 ±0.5 s
(lead free)Depth of immersion: 10mm
www.yageo.com
Dec. 19, 2012 V.6