1104B Series
Single Color PLCC-2 Bathtub Type
(High Reliability type, V-Series)
Reliability Testing Result
Reliability Testing Result Applicable Standard
Testing Conditions
Duration
Failure
Room Temp.
Operating Life
EIAJED-
4701/100(101)
F
Ta = 25 , I = Maxium Rated Current
℃
1,000 h 0/20
1,000 h 0/20
High Temp.
Operating Life
EIAJED-
Ta = Maximum Rated Operating Temperature,
F
4701/100(101) I = Derating Value
Low Temp.
Operating Life
EIAJED-
4701/100(101)
Ta = -40 , I = Maxium Rated Current
1,000 h 0/20
℃
F
Wet High Temp.
Operating Life
EIAJED-
4701/100(102)
F
Ta = 60 , 90%, I = Maxium Rated Current
℃
1,000 h 0/20
Wet High Temp.
Storage Life
EIAJED-
4701/100(103)
Ta = 60 , 90%
℃
1,000 h 0/ 20
EIAJED-
4701/100(105) (each 15min.)
Ta = -40
Maximum Rated Storage Temperature
℃ ~
Thermal Shock
1,000 cycles 0/20
1,000 cycles 0/20
1,000 h 0/ 20
Ta = -40 (off) 85
℃
℃
~
Thermal Shock
Operating
EIAJED-
4701/100(105)
(IF = Derating Value on), (each 15min.)
High Temp.
Storage Life
EIAJED-
4701/200(201)
Ta = Maximum Rated Storage Temperature
Low Temp.
Storage Life
EIAJED-
4701/200(202)
Ta = Minimum Rated Storage Temperature
1,000 h 0/ 20
Ta = -30 (2h)
80 , 95%(2h), 8h/cycle,
℃
℃
~
Cycled Temp.
Humidity Life
EIAJED-
30 cycles 0/20
4701/200(203) IF = Derating Value, 5min on-off
Moisture Soak : 30 , 70%, 72h
℃
Resistance to
Reflow Soldering
EIAJED-
4701/300(301)
Preheat : 150
180 (120s Max.)
Twice 0/ 20
~
℃
Soldering Temp. : 260 (5s)
℃
El ec t r i c St at i c D i sc har ge
EIAJED-
4701/300(304)
C = 100pF, R2 = 1.5K , ±2,000V
Ω
once each polarity 0/ 10
2 h 0/10
1
(ESD )※
Vibration,
Variable Frequency
※1 Reference test
98.1m/s2 (10G), 100
XYZ each direction
2KHz, 20min,
EIAJED-
4701/400(403)
~
Failure Criteria
Items
Symbols
Conditions
Failure criteria
F
I Value of each product
Luminous Intensity
Iv
Testing Min. Value Spec. Min. Value x 0.5
<
Luminous Intensity
F
I Value of each product
F
Forward Voltage
Reverse Current
V
Testing Max. Value Spec. Max. Value x 1.2
≧
Forward Voltage
R
V = Maximum Rated
R
I
Testing Max. Value Spec. Max. Value x 2.5
≧
Reverse Voltage V
Occurrence of notable decoloration,
deformation and cracking
Cosmetic Appearance
-
-
Page 15
2007.8.31