Multilayer Ceramic Capacitors(High Capacitance)
Item
Specification
Test Method
Resistance
Appearance : No mechanical damage
Soldering bath method
to Soldering Capacitance change :
Heat
Preconditioning : Heat treatment(✽1)
Temp. Char. B, X7R, X5R : within 7.5 %
Solder temperature : 270 5 °C
Dipping period : 3.0 0.5 s
Preheat condition :
F, Y5V : within 20 %
tan : Initial standard value
δ
IR : Initial standard value
Withstand voltage : No dielectric breakdown or damage
Order Temp. (°C) Size 0805 max. Size 1206
1
2
80 to 100 120 to 180s 300 to 360s
150 to 200 120 to 180s 300 to 360s
Recovery (Standard condition) : 48 4 h
Solderability More than 95 % of the soldered area of both terminal
electrodes shall be covered with fresh solder.
Soldering bath method
Solder temperature : 230 5 °C
Dipping period : 4 1 s
Solder : H63A (JIS–Z–3282)
Temperature Appearance : No mechanical damage
Preconditioning : Heat treatment(✽1)
Step 1: Minimum operating temp. 30 3 min
Step 2: Room temp. 3 min max.
Cycle
Capacitance change :
Temp. Char. B, X7R, X5R : within 7.5 %
F, Y5V : within 20 %
Step 3: Maximum operating temp. 30 3 min
Step 4: Room temp. 3 min max.
tan : Initial standard value
δ
Number of cycles : 5 cycles
IR : Initial standard value
Recovery(Standard condition) : 48 4 h
Withstand voltage : No dielectric breakdown and/or damage
Damp Heat
Appearance : No mechanical damage
Preconditioning : Heat treatment(✽1)
Temperature : 40 2 °C
(steady state) Capacitance change :
Temp. Char. B, X7R, X5R : within 20 %
Relative humidity : 90 to 95 %
Test period : 500+24/0 h
F, Y5V : within 30 %
tan : Temp. Char. B, X7R, X5R : 0.25 max.
Recovery(Standard condition) : 48 4 h
δ
F, Y5V : 0.3 max.
IR : 50/C (M ) min.
ȑ
Note : 10/C (M ) min. for rated vol. DC 10 V max.
C:Nominal cap. in µF
ȑ
Please see the technical specifications for details.
Damp Heat
Load
Appearance : No mechanical damage
Capacitance change :
Preconditioning : Voltage treatment(✽2)
Temperature : 40 2 °C
Temp. Char. B, X7R, X5R : within 20 %
F, Y5V : within 30 %
Relative humidity : 90 to 95 %
Applied voltage : Rated voltage
Charge/discharge current : 50 mA max.
Test period : 500+24/0 h
tan : Temp. Char. B, X7R, X5R : 0.25 max.
δ
F, Y5V : 0.3 max.
IR : 25/C (M ) min.
Recovery(Standard condition) : 48 4 h
ȑ
Note : 5/C (M ) min. for rated vol. DC 10 V max.
ȑ
C:Nominal cap. in µF
Please see the technical specifications for details.
High
Appearance : no mechanical damage
Preconditioning : Voltage treatment(✽2)
Temperature Capacitance change :
Temperature : Maximum operation temp. 3 °C
Load
Temp. Char. B, X7R, X5R : within 20 %
Applied voltage : (1)Rated voltage 200 %
҂
F, Y5V : within 30 %
(2)Rated voltage 150 %
҂
tan : Temp. Char. B, X7R, X5R : 0.25 max.
(3)Rated voltage 100 %
δ
҂
F, Y5V : 0.3 max.
Please see the technical specifications
for details.
IR : 50/C (M ) min.
ȑ
Note : 10/C (M ) min. for rated vol. DC 10 V max.
C:Nominal cap. in µF
Charge/discharge current : 50 mA max.
Test period : 1000+48/0 h
ȑ
Please see the technical specifications for details.
Recovery (Standard condition) : 48 4 h
(✽1) Heat treatment : 1 h of heat treatment at 150+0/–10 °C followed by 48 4 h recovery under standard conditions.
(✽2)Voltage treatment : 1 h of voltage treatment under the specified temperature and voltage for testing followed by 48 4 h of recovery under
standard conditions.