6.RELIABILITY
(1) TEST ITEMS AND RESULTS
Standard
Number of
Test Item
Resistance to
Soldering Heat
(Reflow Soldering)
Solderability
Test Method
JEITA ED-4701
300 301
Test Conditions
Tsld=260°C, 10sec.
(Pre treatment 30°C,70%,168hrs.)
Note
2 times
Damaged
0/50
JEITA ED-4701
300 303
JEITA ED-4701
300 307
JEITA ED-4701
100 105
JEITA ED-4701
200 203
JEITA ED-4701
200 201
JEITA ED-4701
100 103
JEITA ED-4701
200 202
Tsld=215 ± 5°C, 3sec.
(Lead Solder)
0°C ~ 100°C
1 time
over 95%
20 cycles
0/50
0/50
0/50
0/50
0/50
0/50
0/50
0/50
0/50
0/50
0/50
0/50
0/50
(Reflow Soldering)
Thermal Shock
15sec. 15sec.
Temperature Cycle
-40°C ~ 25°C ~ 100°C ~ 25°C
30min. 5min. 30min. 5min.
25°C ~ 65°C ~ -10°C
90%RH 24hrs./1cycle
Ta=100°C
100 cycles
10 cycles
1000 hrs.
1000 hrs.
1000 hrs.
1000 hrs.
500 hrs.
Moisture Resistance Cyclic
High Temperature Storage
Temperature Humidity
Storage
Low Temperature Storage
Ta=60°C, RH=90%
Ta=-40°C
Steady State Operating Life
Condition 1
Steady State Operating Life
Condition 2
Steady State Operating Life
of High Temperature
Steady State Operating Life
of High Humidity Heat
Steady State Operating Life
of Low Temperature
Vibration
Ta=25°C, IF=20mA
Ta=25°C, IF=35mA
Ta=85°C, IF=8.5mA
60°C, RH=90%, IF=15mA
Ta=-30°C, IF=20mA
1000 hrs.
500 hrs.
1000 hrs.
48min.
JEITA ED-4701
400 403
100 ~ 2000 ~ 100Hz Sweep 4min.
200m/s2
3directions, 4cycles
3mm, 5 ± 1 sec.
Substrate Bending
Adhesion Strength
JEITA ED-4702
JEITA ED-4702
1 time
1 time
0/50
0/50
5N, 10 ± 1 sec.
(2) CRITERIA FOR JUDGING DAMAGE
Criteria for Judgement
Min. Max.
Item
Symbol Test Conditions
Forward Voltage
Reverse Current
Luminous Intensity
VF
IR
IF=20mA
-
U.S.L.*)¯ 1.1
U.S.L.*)¯ 2.0
-
VR=5V
-
IV
IF=20mA
L.S.L.**)¯ 0.7
*) U.S.L. : Upper Standard Level
**) L.S.L. : Lower Standard Level