• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
!Note
!Note
C02E.pdf
10.12.20
sales representatives or product engineers before ordering.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
GRM Series Specifications and T st Methods (2) (Note 1)-Typical Inspection
GRM Series Specifications and Test Methods (2) (Note 1)-Typical Inspection
(Note 1) These Specifications and Test Methods indicate typical inspection.
Please refer to individual specifications (our product specifications or the approval sheet).
When no "*" is added in PNs table, please refer to GRM Series Specifications and Test Methods (1).
Continued from the preceding page.
When "*" is added in PNs table, please refer to GRM Series Specifications and Test Methods (2).
No.
Item
Specifications
B1, B3 : Within ±10% (–25 to +85°C)
Test Method
The capacitance change should be measured after 5 min. at
each specified temp. stage.
F1
R6
: Within +30/–80% (–25 to +85°C)
: Within ±15% (–55 to +85°C)
The ranges of capacitance change compared with the
reference temperature value over the temperature ranges
shown in the table should be within the specified ranges.*
In case of applying voltage, the capacitance change should be
measured after 1 more min. with applying voltage in
equilibration of each temp. stage.
R1, R7 : Within ±15% (–55 to +125°C)
F5
: Within +22/–82% (–30 to +85°C)
: Within ±22% (–55 to +85°C)
No bias C6
C7
C8
D7
E7
D8
: Within ±22% (–55 to +125°C)
: Within ±22% (–55 to +105°C)
: Within +22/–33% (–55 to +125°C)
: Within +22/–56% (–55 to +125°C)
: Within +22/–33% (–55 to +105°C)
*GRM32DR60J226, GRM43 B1/B3/R6 0J/1A 336/476: 1.0±0.2Vrms
GRM155B30G475, GRM155B30J 225, GRM21BB30J476,
GRM155R60E106, GRM188 B3/R6 0E/0G/0J 226: 0.2±0.05Vrms
Step
Temperature (°C)
Applying Voltage (V)
25±2 (for R6, R7, C6, C7, C8, D7, D8, E7, F5
20±2 (for B1, B3, F1, R1)
)
1
–55±3 (for R1, R6, R7, C6, C7, C8, D7, D8, E7
–30±3 (for F5)
–25±3 (for B1, B3, F1)
)
Capacitance
Temperature
Characteristics
2
3
4
9
No bias
25±2 (for R6, R7, C6, C7, C8, D7, D8, E7, F5
20±2 (for B1, B3, F1, R1)
)
125±3 (for R1, R7, C7, D7, E7)
105±3 (for C8, D8)
50% of
B1: Within +10/–30%
85±3 (for B1, B3, F1, F5, R6, C6)
the Rated R1: Within +15/–40%
Voltage
F1: Within +30/–95%
5
6
7
8
20±2 (for B1, F1, R1)
–55±3 (for R1)
–25±3 (for B1, F1)
20±2 (for B1, F1, R1)
125±3 (for R1)
85±3 (for B1, F1)
50% of the
rated voltage
•Initial measurement for high dielectric constant type
Perform a heat treatment at 150 +0/–10°C for one hour and
then set for 24±2 hours at room temperature.
Perform the initial measurement.
Solder the capacitor on the test jig (glass epoxy board) shown
in Fig. 1a using a eutectic solder. Then apply 10N* force in
parallel with the test jig for 10±1sec.
The soldering should be done either with an iron or using the
reflow method and should be conducted with care so that the
soldering is uniform and free of defects such as heat shock.
*1N: GRM02, 2N: GRM03, 5N: GRM15/GRM18
No removal of the terminations or other defects should occur.
c
Type
GRM02
a
b
c
Adhesive Strength
of Termination
10
0.2
0.3
0.4
1.0
1.2
2.2
2.2
3.5
4.5
0.56
0.9
1.5
3.0
4.0
5.0
5.0
7.0
8.0
0.23
0.3
0.5
1.2
1.65
2.0
2.9
3.7
5.6
GRM03
GRM15
GRM18
GRM21
GRM31
GRM32
GRM43
GRM55
Solder resist
Baked electrode or
copper foil
Fig. 1a
Appearance
Capacitance
No defects or abnormalities
Within the specified tolerance
Solder the capacitor on the test jig (glass epoxy board) in the
same manner and under the same conditions as (10).
The capacitor should be subjected to a simple harmonic motion
having a total amplitude of 1.5mm, the frequency being varied
uniformly between the approximate limits of 10 and 55Hz. The
frequency range, from 10 to 55Hz and return to 10Hz, should
be traversed in approximately 1 minute. This motion should be
applied for a period of 2 hours in each of 3 mutually
B1, B3, R1, *R6, *R7, C7, C8, E7, D7: 0.1 max.
C6: 0.125 max.
D8: 0.15 max.
F1, F5: 0.2 max.
*GRM31CR71E106: 0.125 max.
GRM31CR6 0J/0G 107: 0.15 max.
11 Vibration
D.F.
perpendicular directions (total of 6 hours).
Continued on the following page.
58