• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
1. This Specifications and Test Methods is downloaded from the website of Murata Manufacturing co.,ltd. Therefore, it's specifications are subject to change or our products in it may be discontinued without advance noCtice0. 2E.pdf
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
!Note
!Note
sales representatives or product engineers before ordering.
0. Please check with our sales representatives or product engineers before ordering.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
2. This Specifications and Test Methods has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product
10.12.20
0. specifications before ordering.
GNM Series Specifications and Test Methods (1)
When no "*" is added in PNs table, please refer to GNM Series Specifications and Test Methods (1).
Continued from the preceding page.
When "*" is added in PNs table, please refer to GNM Series Specifications and Test Methods (2).
Specifications
No.
Item
Test Method
Temperature
Compensating Type
High Dielectric Type
Temperature
Cycle
The measured and observed characteristics should satisfy the
specifications in the following table.
Fix the capacitor to the supporting jig in the same manner and
under the same conditions as (10). Perform the five cycles
according to the four heat treatments listed in the following
table. Let sit for 24±2 hours (temperature compensating type)
or 48±4 hours (high dielectric constant type) at room
temperature, then measure.
Appearance No marking defects
Within ±2.5%
or ±0.25pF
Capacitance
R7, R6, C7: Within ±7.5%
Change
(whichever is
larger)
Step
1
2
3
4
30pF min.: QU1000
30pF max.:
15
Min.
Max.
Room
Temp.
Room
Temp.
Temp. (°C) Operating
Operating
Temp. +3/–0
30±3
Char. 25V min. 16V
R7, R6, 0.025 0.035 0.035 0.05
C7 max. max. max. max.
10V
6.3V
QU400+20C
Temp.+0/–3
Q/D.F.
I.R.
Time (min.)
30±3
2 to 3
2 to 3
C:Nominal
• Initial measurement for high dielectric constant type
Capacitance (pF)
Perform a heat treatment at 150+0/-10°C for one hour and
then let sit for 24±2 hours at room temperature.
Perform the initial measurement.
More than 10,000MΩ or 500Ω · F (whichever is smaller)
Dielectric
Strength
No failure
Humidity Steady
State
The measured and observed characteristics should satisfy the
specifications in the following table.
Appearance No marking defects
Within ±5%
or ±0.5pF
Capacitance
Change
R7, R6, C7: Within ±12.5%
(whichever is
larger)
Set the capacitor at 40±2°C and 90 to 95% humidity for 500±12
30pF and over:
hours.
16
QU350
Remove and let sit for 24±2 hours at room temperature, then
10pF and over,
30pF and below:
QU275+5C/2
10pF and below:
QU200+10C
measure.
Char. 25V min. 16V
10V/6.3V
0.05
max.
Q/D.F.
R7, R6,
C7
0.05
max.
0.05
max.
C: Nominal
Capacitance (pF)
I.R.
More than 1,000MΩ or 50Ω · F (whichever is smaller)
The measured and observed characteristics should satisfy the
specifications in the following table.
Humidity Load
Appearance No marking defects
Within ±7.5%
or ±0.75pF
Capacitance
Change
R7, R6, C7: Within ±12.5%
(whichever is
larger)
Apply the rated voltage at 40±2°C and 90 to 95% humidity for
500±12 hours.
17
Remove and let sit for 24±2 hours at room temperature, then
measure.
The charge/discharge current is less than 50mA.
30pF and over:
QU200
30pF and below:
Char. 25V min. 16V
10V/6.3V
Q/D.F.
I.R.
QU100+10C/3
R7, R6,
C7
0.05
max.
0.05
max.
0.05
max.
C: Nominal
Capacitance (pF)
More than 500MΩ or 25Ω · F (whichever is smaller)
Continued on the following page.