• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our
• Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
!Note
!Note
C02E.pdf
10.12.20
sales representatives or product engineers before ordering.
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
GRM Series Specifications and Test M thods (2) (Note 1)-Typical Inspection
GRM Series Specifications and Test Methods (2) (Note 1)-Typical Inspection
(Note 1) These Specifications and Test Methods indicate typical inspection.
Please refer to individual specifications (our product specifications or the approval sheet).
When no "*" is added in PNs table, please refer to GRM Series Specifications and Test Methods (1).
Continued from the preceding page.
When "*" is added in PNs table, please refer to GRM Series Specifications and Test Methods (2).
No.
Item
Specifications
Test Method
Appearance
No marking defects
Within ±10%
Solder the capacitor on the test jig (glass epoxy board) shown
in Fig. 2a using a eutectic solder. Then apply a force in the
direction shown in Fig. 3a for 5±1 sec. The soldering should be
done by the reflow method and should be conducted with care
so that the soldering is uniform and free of defects such as heat
shock.
Capacitance
Change
b
ø4.5
c
20
Pressurizing
speed: 1.0mm/sec.
50
Pressurize
a
R230
100
t: 1.6mm
12 Deflection
Fig. 2a
Flexure : V1
(GRM02/03/15: t: 0.8mm)
Type
GRM02
a
b
c
Capacitance meter
0.2
0.3
0.4
1.0
1.2
2.2
2.2
3.5
4.5
0.56
0.9
1.5
3.0
4.0
5.0
5.0
7.0
8.0
0.23
0.3
0.5
1.2
1.65
2.0
2.9
3.7
5.6
45
45
GRM03
GRM15
GRM18
GRM21
GRM31
GRM32
GRM43
GRM55
Fig.3a
(in mm)
Immerse the capacitor in a solution of ethanol (JIS-K-8101) and
rosin (JIS-K-5902) (25% rosin in weight proportion).
Preheat at 80 to 120°C for 10 to 30 seconds.
After preheating, immerse in a eutectic solder solution for
2±0.5 seconds at 230±5°C or Sn-3.0Ag-0.5Cu solder solution
for 2±0.5 seconds at 245±5°C.
Solderability of
Termination
75% of the terminations is to be soldered evenly and
continuously.
13
Appearance
No defects or abnormalities
B1, B3, R1, *R6, R7, C6, C7, *C8, E7, D7, D8: Within ±7.5%
F1, F5: Within ±20%
Preheat the capacitor at 120 to 150°C for 1 minute.
Immerse the capacitor in a eutectic solder* or Sn-3.0Ag-0.5Cu
solder solution at 270±5°C for 10±0.5 seconds. Set at room
temperature for 24±2 hours, then measure.
Capacitance
Change
*GRM188R6 0J/0G 106, GRM188C8 0E/0G 106, GRM219R60G226:
Within ±12.5%
GRM155R60G475, GRM155R60E106, GRM188R60G226:
Within ±15%
*Do not apply to GRM02.
Resistance
to
Soldering
Heat
•Initial measurement for high dielectric constant type
Perform a heat treatment at 150+0/–10°C for one hour and
then set at room temperature for 24±2 hours.
Perform the initial measurement.
B1, B3, R1, *R6, *R7, C7, C8, E7, D7: 0.1 max.
C6: 0.125 max.
D8: 0.15 max.
F1, F5: 0.2 max.
*GRM31CR71E106: 0.125 max.
GRM31CR6 0J/0G 107: 0.15 max.
14
D.F.
I.R.
*Preheating for GRM32/43/55
Step
1
2
Temperature
100 to 120°C
170 to 200°C
Time
1 min.
1 min.
More than 50Ω · F
No defects
Dielectric
Strength
Appearance
No defects or abnormalities
Fix the capacitor to the supporting jig in the same manner and
under the same conditions as (10).
Perform the five cycles according to the four heat treatments
shown in the following table.
B1, B3, R1, R6, R7, C6, C7, C8, D7, D8: Within ±7.5%
E7: Within ±30%
F1, F5: Within ±20%
Capacitance
Change
Set for 24±2 hours at room temperature, then measure.
B1, B3, R1, *R6, *R7, C7, C8, E7, D7: 0.1 max.
C6: 0.125 max.
D8: 0.15 max.
Step
1
2
3
4
Min.
Max.
Operating
Temp. +3/–0
Room
Temp.
Room
Temp.
Temperature
Temp. (°C) Operating
D.F.
I.R.
F1, F5: 0.2 max.
Temp. +0/–3
15 Sudden
Change
*GRM31CR71E106: 0.125 max.
GRM31CR6 0J/0G 107: 0.15 max.
Time (min.)
30±3
2 to 3
30±3
2 to 3
•Initial measurement for high dielectric constant type
More than 50Ω · F
Perform a heat treatment at 150+0/–10°C for one hour and
then set at room temperature for 24±2 hours.
Perform the initial measurement.
Dielectric
Strength
GRM188R60J106 only Measurement after test Perform a heat
treatment and then let sit for 24±2 hours at room temperature,
then measure.
No defects
Continued on the following page.