■ Specifications and Test Methods
No Item
Specification
Test Method(Ref. Standard:JIS C 5101, IEC60384）
No removal of the terminations or other defect should occur.
Mounting method
Applied Force
Solder the capacitor on the test substrate
2N
9 Adhesive Strength of
Termination
Holding Time
10+/-1s
Applied Direction
In parallel with the test substrate and vertical with the capacitor side
Appearance
Capacitance
Q or D.F.
No defects or abnormalities.
Within the specified initial value.
Within the specified initial value.
Mounting method
Kind of Vibration
Vibration Time
Solder the capacitor on the test substrate
A simple harmonic motion 10Hz to 55Hz to 10Hz
1min
10 Vibration
Total amplitude
1.5mm
Vibration directions and time
This motion should be applied for a period of 2hours in each 3 mutually
perpendicular directions(total of 6hours).
Appearance
Capacitance Change
No defects or abnormalities.
Within +/-10%
Mounting method
Pressurization Method
Flexure
Reflow solder the capacitor on the test substrate
Shown in Fig.2
1mm
11 Substrate Bending test
12 Solderability
Holding Time
5+/-1s
95% of the terminations is to be soldered evenly and continuously.
Test Method
Flux
Preheat
Kind of Solder
Test Temperature
Test Time
Solder bath method
Solution of rosin ethanol 25(mass)%
80℃ to 120℃、10s to 30s
Sn-3.0Ag-0.5Cu(Lead Free Solder)
245+/-5℃
2+/-0.5s
Appearance
Capacitance Change
Q or D.F.
I.R.
Voltage proof
No defects or abnormalities.
Within +/-7.5%
Within the specified initial value.
Within the specified initial value.
No defects or abnormalities.
Pre-treatment
Heat treatment:Perform a heat treatment at 150+0/-10°C for 1hour and then let sit for 24+/-2hours
at room temperature, then measure.
Solder bath method
Sn-3.0Ag-0.5Cu(Lead Free Solder)
270+/-5℃
10+/-0.5s
13 Resistance to Soldering
Heat
Test Method
Kind of Solder
Test Temperature
Test Time
Preheat Temperature
Preheat time
120℃ to 150℃
1 min
Post-treatment
Non treatment:Let sit for 24+/-2hours at room temperature, then measure.
Appearance
Capacitance Change
Q or D.F.
I.R.
Voltage proof
No defects or abnormalities.
Within +/-7.5%
Within the specified initial value.
Within the specified initial value.
No defects or abnormalities.
Mounting method
Pre-treatment
Solder the capacitor on the test substrate
Heat treatment:Perform a heat treatment at 150+0/-10°C for 1hour and then let sit for 24+/-2hours
at room temperature, then measure.
5cycles
14 Temperature Sudden
Change
Cycles
Temperature Cycling
Post-treatment
Non treatment:Let sit for 24+/-2hours at room temperature, then measure.