General Specifications
Environmental
STEADY STATE HUMIDITY
(No Load)
Insulation Resistance
C0G (NP0), X7R: To meet initial value x 0.3
Z5U, Y5V: ≥ Initial Value x 0.1
Specification
Charge devices with rated voltage in test chamber set
Appearance
at 85
5% relative humidity and 85°C for 1000
No visual defects
(+48,-0) hours. Remove from test chamber and
Capacitance Variation
C0G (NP0): 5% or .5pF, whichever is greater
X7R: ≤ 10%
stabilize at room temperature and humidity for 48
hours (24 2 hours for C0G (NP0)) before measuring.
4
Charge and discharge currents must be less than
50ma.
Z5U: ≤ 30%
Y5V: ≤ 30%
Q, Tan Delta
C0G (NP0): ≥ 30pF......................Q ≥ 350
≥ 10pF, < 30pF.........Q ≥ 275+5C/2
< 10pF ....................Q ≥ 200+10C
X7R: Initial requirement + .5%
Z5U: Initial requirement + 1%
Y5V: Initial requirement + 2%
LOAD LIFE
Specification
Appearance
No visual defects
Insulation Resistance
≥ Initial Value x 0.3
Measuring Conditions
Capacitance Variation
C0G (NP0): 3% or .3pF, whichever is greater
X7R: ≤ 10%
Z5U: ≤ 30%
Y5V: ≤ 30%
Q, Tan Delta
C0G (NP0): ≥ 30pF......................Q ≥ 350
≥ 10pF, < 30pF.........Q ≥ 275+5C/2
< 10pF ....................Q ≥ 200+10C
X7R: Initial requirement + .5%
Z5U: Initial requirement + 1%
Y5V: Initial requirement + 2%
Store at 85 5% relative humidity and 85°C for 1000
hours, without voltage. Remove from test chamber
and stabilize at room temperature and humidity for
48 4 hours (24 2 hours for C0G (NP0)) before
measuring.
Charge and discharge currents must be less than
50ma.
Insulation Resistance
C0G (NP0), X7R: To meet initial value x 0.3
Z5U, Y5V: ≥ Initial Value x 0.1
LOAD HUMIDITY
Specification
Charge devices with twice rated voltage in test
chamber set at +125°C 2°C for C0G (NP0) and X7R,
+85° 2°C for Z5U, and Y5V for 1000 (+48,-0) hours.
Remove from test chamber and stabilize at room
temperature for 48 4 hours (24 2 hours for C0G
(NP0)) before measuring.
Appearance
No visual defects
Capacitance Variation
C0G (NP0): 5% or .5pF, whichever is greater
X7R: ≤ 10%
Z5U: ≤ 30%
Y5V: ≤ 30%
Charge and discharge currents must be less than
50ma.
Q, Tan Delta
C0G (NP0): ≥ 30pF .....................Q ≥ 350
≥ 10pF,< 30pF.........Q ≥ 275+5C/2
< 10pF ....................Q ≥ 200+10C
X7R: Initial requirement + .5%
Z5U: Initial requirement + 1%
Y5V: Initial requirement + 2%
23