PHYSICAL PROPERTIES
Property
Mechanical
Test Method
Condition
Unit
Tensile strength at yield
Tensile strength at break
Tensile strain at yield
Tensile strain at break
Flexual modulus
ASTM D 638
ASTM D 638
ASTM D 638
ASTM D 638
50mm/min
50mm/min
50mm/min
50mm/min
MPa
MPa
%
62
68
7
%
130
2340
96
ASTM D 790 1.3mm/min, 50mm span
ASTM D 790 1.3mm/min, 50mm span
MPa
MPa
J/m
J/m
-
Flexual strength at yield
ASTM D 4812
ASTM D 256
ASTM D 785
unnoched
noched
3204
801
70
Izot impact
Rockwell hardness
Thermal
M scale
1.82MPa
0.45MPa
℃
℃
132
137
154
10.5
Heat deflection temperature
6.4mm, unannealed
ASTM D 648
Vicat softening point
Melt flow rate
ASTM D 1525
ASTM D 1236
B/50
℃
300℃/1.2kgf
g/10min
Electrical
>1017
14.9
Volume resistivity
Dielectric strength
ASTM D 257
ASTM D 149
-
Ωm
in air, 3.2mm
50/60Hz
1MHz
kV/mm
-
-
-
-
3.17
Relative permittivity
Dissipation factor
ASTM D 150
ASTM D 150
2.96
50/60Hz
1MHz
0.0009
0.01
Other
g/cm3
Density
ASTM D 792
ASTM D 570
UL94
-
1.19
0.15
0.35
HB
24h
%
%
Water absorption
23℃/equilibrium
-
Flammability
class
*Values reported are typical and should not be used for specification purpose.
Ref.CE-P680 03/10